Felicitas Schröder

• This work presents the synthesis and characterization of metallic, catalytically relevant nanoparticles in the metal-organic framework MOF-5, with a focus on the investigation of host-guest interactions. Ru nanoparticles in MOF-5 were obtained via hydrogenolysis of [Ru(cod)(cot)]@MOF-5. The particles showed a behavior similar to surfactant stabilized Ru colloids in solution, exhibiting very low interactions with the host matrix MOF-5. In addition, simultaneous loading of MOF-5 with two different MOCVD precursors was performed, including cohydrogenolysis of \([Pt(cod)Me_{2}]/[Ru(cod)(cot)]\) in MOF-5. Hints for the formation of a \(Pt_{50}Ru_{50}\) alloy in MOF-5 were found. Investigations on the MOF-5-water interactions confirmed the sensitivity of MOF-5 towards even small amounts (4 wt.%) of water.
• Die Arbeit befasst sich mit der Synthese und mikrostrukturellen Charakterisierung von metallischen, katalytisch relevanten Nanopartikeln im metallorganischen Netzwerk MOF-5, mit Schwerpunkt auf die vorherrschenden Wirt-Gast Wechselwirkungen. Ausgehend von [Ru(cod)(cot)]@MOF-5 konnten Ru Nanopartikel in MOF-5 hydrogenolytisch erhalten werden, dabei verhielten sich die Partikel ähnlich wie in Lösung stabilisierte Ru Kolloide und zeigten sehr geringe Wechselwirkungen mit der Trägermatrix. Weiterhin wurde die simultane Beladung von MOF-5 mit zwei verschiedenen MOCVD Precursoren durchgeführt, einschließlich der Cohydrogenolyse von \([Pt(cod)Me_{2}]/[Ru(cod)(cot)]\) in MOF-5, dabei wurden Hinweise auf eine mögliche \(Pt_{50}Ru_{50}\) Legierung in MOF-5 gefunden. Untersuchungen zur Wechselwirkungen von MOF-5 mit \(H_{2}O\) bestätigten die hohe Sensibilität von MOF-5 gegenüber selbst geringen Mengen von Wasser (4 wt.%).