Anastasia Dushina

• In this thesis, the electrochemical properties of the various aqueous electrolytes, cathodes and anodes materials were investigated. The stability window of the different electrolytes was determined by the chronopotentiometry in anodic and cathodic domains separately. Based on these results, the influence of pH value, gellification, ions and solvents on the stability window of the solutions was investigated in details. In addition, the suitable for aqueous electrolyte cathodes materials, including LiMn\(_{2}\)O\(_{4}\), LiCoO\(_{2}\) and LiMn\(_{2}\)O\(_{4}\), were developed in this work by studying their electrochemical performance. It was observed that capacity fading upon cycling depends on many factors including the method of formation and material synthesis, current collector of material, its thickness and coating.
• In dieser Doktorarbeit wurden die elektrochemischen Eigenschaften von den verschiedenen Elektrolyten, Kathoden und Anoden Materialien untersucht. Die Stabilitätsfenster der verschiedenen Elektrolyte wurden durch die Chronopotentiometrie in den anodischen und kathodischen Domains separat bestimmt. Basierend auf diesen Ergebnissen, wie dem Einfluss von pH-Wert, der Gelierung, den Ionen und Lösungsmittel auf das Stabilitätsfenster der Lösungen wurden im Detail entwickelt. Die geeigneten kathodischen Materialien für die wässrigen Elektrolyte, einschließlich LiMn\(_{2}\)O\(_{4}\), LiCoO\(_{2}\) and LiMn\(_{2}\)O\(_{4}\), wurden durch ihre elektrochemische Leistung in dieser Arbeit erforscht. Es wurde beobachtet, dass der Kapazitätsverlust von vielen Faktoren abhängt, einschließlich des Herstellungsverfahrens und der Materialsynthese, dem Stromabnehmer, der Materialdicke und der Art der Beschichtung.